报告题目:Formation of Durable Interphase Layer on Lithium Metal for High-Performance Lithium-Sulfur Batteries

报告时间:2017年12月15日(星期五)上午9:00-11:00

报告地点:能源楼1号楼一楼会议室

报告人:WANG Donghai, Pennsylvania State University, USA

  报告人简介:

  Dr. WANG Donghai is currently Associate Professor at Department of Mechanical Engineering and Department of Chemical Engineering at The Pennsylvania State University. Before joining Penn State in 2009, he was a postdoc and subsequently became a staff scientist at Pacific Northwest National Laboratories where he developed functional materials for catalysis and energy storage techniques. He received a B.S. and Ph.D. degree in Chemical Engineering from Tsinghua University and Tulane University in 1997 and 2006, respectively. Dr. WANG Donghai’s research interests have been related to design and synthesis of materials for a variety of applications. His recent research is focused on material development for energy conversion and storage technologies such as batteries, supercapacitors, fuel cells and solar fuels. Professor WANG has authored and co-authored over 90 peer reviewed publications, more than 15 patents and patent applications, and 4 book chapters.

  报告摘要:

  In this talk, he will present strategies to reinforce the solid-electrolyte interphase (SEI) with desired properties including good tolerance to the Li interface change and efficient surface passivation against electrolyte penetration. The approach works via either introducing multiple functional components bonded to the Li surface into the SEI or depositing flexible organic/inorganic hybrid coating layer. This self-forming of the reinforced SEI can be triggered once fresh Li is deposited at the interface, thus realizing a lasting formation of the stable SEI. The as-formed durable SEI layer can suppress dendritic Li growth, enhance Li plating/stripping CE, and in turn, enable Li-S batteries with long cycling life and good capacity retention. He will also demonstrate the reinforced SEI can improve Li metal efficiency in a carbonate-based electrolyte for Li-metal oxide batteries. This study provides a promising route to address the issues associated with Li metal anodes and promote the development of high-energy rechargeable Li metal batteries.

  联系人:DNL17 刘慧颖

  联系电话:84379536

打印】  【关闭】  【返回
Copyright © 1999-2017. Dalian Institute of Chemical Physics, Chinese Academy of Sciences.
辽ICP备05000861号 辽公网安备21020402000367号
中国科学院大连化学物理研究所 版权所有 All rights reserved.